The study focuses on the flexural response of concurrently 3D printed sandwich composites with a syntactic foam core. Sandwich structures with syntactic foam cores are considered promising in marine applications due to their lower water uptake in the foam core when faced with damage to the face-sheets. In this research, high-density polyethylene (HDPE) filament is used to 3D print the skin of the sandwich, while glass microballoon (GMB) reinforced HDPE syntactic foam filaments are utilized for the core. To optimize the parameters, blends of GMB in HDPE are prepared at different volume percentages: 20%, 40%, and 60%. These foamed blends are then extruded into filament form for use in commercially available fused filament fabrication (FFF) based 3D printers. The defect-free syntactic foam core sandwich composites are concurrently 3D printed to characterize their flexural behavior. The printed HDPE, foam cores, and sandwiches undergo testing under a three-point bending mode. The results show that the addition of GMB increases both specific modulus and strength in the sandwich composites, with the highest improvement observed in sandwiches containing a core with a volume percentage of 60% GMB. Additionally, the flexural strength, fracture strength, and strain of foam core sandwiches exhibit a superior response compared to their respective cores. The experimental results align well with theoretical predictions. Finally, the failure mode of the printed sandwich is also discussed in detail. Overall, this study provides valuable insights into the flexural response of concurrently 3D printed sandwich composites with a focus on optimizing material composition and understanding their mechanical properties. The findings contribute to advancements in lightweight materials for marine applications and demonstrate the potential benefits of using syntactic foam cores in sandwich structures.

• - Study focuses on flexural response of concurrently 3D printed sandwich composites with a syntactic foam core
• - Sandwich structures with syntactic foam cores are promising in marine applications due to lower water uptake in the foam core when faced with damage to face-sheets
• - High-density polyethylene (HDPE) filament used to 3D print skin of sandwich
• - Glass microballoon (GMB) reinforced HDPE syntactic foam filaments used for the core
• - Blends of GMB in HDPE prepared at different volume percentages: 20%, 40%, and 60%
• - Foamed blends extruded into filament form for use in commercially available fused filament fabrication (FFF) based 3D printers
• - Defect-free syntactic foam core sandwich composites concurrently 3D printed for characterization of flexural behavior
• - Addition of GMB increases specific modulus and strength in sandwich composites, highest improvement observed in sandwiches containing a core with a volume percentage of 60% GMB
• - Flexural strength, fracture strength, and strain of foam core sandwiches exhibit superior response compared to their respective cores
• - Experimental results align well with theoretical predictions
• - Failure mode of printed sandwich discussed in detail
• - Study provides valuable insights into flexural response of concurrently 3D printed sandwich composites, optimizing material composition, and understanding mechanical properties
• - Findings contribute to advancements in lightweight materials for marine applications and demonstrate potential benefits of using syntactic foam cores in sandwich structures.

This study is about how 3D printed sandwich structures with a special foam inside bend when they are pushed or pulled. The foam inside the sandwich helps it not absorb too much water if it gets damaged in water. The outside of the sandwich is made from a type of plastic called high-density polyethylene (HDPE). The foam inside the sandwich is made from HDPE mixed with tiny glass balls called glass microballoons (GMB). Different mixtures of GMB and HDPE were used to make the foam. The foam was then turned into a long string that can be used in 3D printers. The researchers made sandwiches using this foam and tested how strong they were when bent. They found that adding more GMB made the sandwiches stronger, especially when there was 60% GMB in the foam. The sandwiches were stronger than just the foam by itself. The results matched what they expected based on their calculations. They also looked at how the sandwiches broke and talked about it in detail. This study gives us important information about making strong 3D printed sandwiches and understanding their properties. It can help make better materials for boats and other things that go in water."

3D Printed Sandwich Composites with Syntactic Foam Core: Optimizing Material Composition and Understanding Mechanical Properties

The use of lightweight materials in marine applications is a growing area of research, as lighter structures can reduce fuel consumption and increase the efficiency of vessels. One promising material for this purpose is sandwich composites with syntactic foam cores. These sandwiches have lower water uptake when faced with damage to the face-sheets, making them ideal for marine applications. In this study, researchers investigate the flexural response of concurrently 3D printed sandwich composites with a syntactic foam core. High-density polyethylene (HDPE) filament was used to 3D print the skin of the sandwich, while glass microballoon (GMB) reinforced HDPE syntactic foam filaments were utilized for the core. To optimize parameters, blends of GMB in HDPE were prepared at different volume percentages: 20%, 40%, and 60%. These foamed blends were then extruded into filament form for use in commercially available fused filament fabrication (FFF) based 3D printers. The defect-free syntactic foam core sandwiches were concurrently 3D printed to characterize their flexural behavior under three-point bending mode testing.

Results

The results showed that adding GMB increased both specific modulus and strength in the sandwich composites, with highest improvement observed in sandwiches containing a core with a volume percentage of 60% GMB. Additionally, flexural strength, fracture strength, and strain all exhibited superior responses compared to their respective cores alone. The experimental results aligned well with theoretical predictions made by researchers prior to testing. Finally, failure mode analysis revealed that delamination between face sheets was responsible for most failures observed during testing; however some fractures occurred within face sheets due to excessive loading or poor printing quality near edges or corners where stress concentrations occur more easily than other areas on flat surfaces due to geometric discontinuities like sharp edges or corners which are prone to higher stresses than flat surfaces under similar loading conditions .

Conclusion

Overall, this study provides valuable insights into optimizing material composition and understanding mechanical properties related to flexural response when using concurrently 3D printed sandwich composites with a focus on syntactic foam cores for marine applications. The findings contribute significantly towards advancements in lightweight materials suitable for such applications and demonstrate potential benefits associated with using these types of structures over traditional ones without synthetic foam cores