The researchers in this study utilized Carr-Purcell-Meiboom-Gill (CPMG) dynamical decoupling to investigate the magnetic noise power spectra for ensembles of P1 and NV centers in diamond using pulsed electron paramagnetic resonance (pEPR) at 2.5 GHz. The experiments were conducted on both HPHT (high pressure, high temperature) diamond samples and CVD (chemical vapor deposition) diamond samples at different magnetic field strengths. The results revealed that interactions with 13C nuclei dominated and obscured the broad features of the NV power spectrum at 13 mT. However, increasing the magnetic field to 190 mT reduced the effect of these interactions, allowing the background noise to exhibit a 1/ω spectrum. This behavior was also observed with P1 centers in the CVD sample. A comparison was made with previous measurements on single spins and small ensembles, showing a high-frequency tail from a Lorentzian power spectrum. Furthermore, the researchers characterized the resonant 13C Larmor frequency feature for both P1 centers at 89 mT and NV centers at 190 mT by introducing a filter function-based protocol for measuring sharp features in the power spectrum at frequencies higher than the maximum CPMG modulation frequency accessible with the system hardware. The manuscript is structured into different sections: Section II describes the basic framework for their experiments, Section III summarizes the theoretical model describing coherence decay under application of a DD pulse sequence, and Section IV presents key results including an overview of experimental data, analysis of background noise, and characterization of resonant peaks. Finally, Section V summarizes their findings and provides insights into future experiments. Overall,this study provides valuable insights into understanding magnetic noise power spectra for ensembles of P1 and NV centers in diamond under different experimental conditions. The techniques developed in this research could have implications for various applications such as ac magnetometry and noise spectroscopy measurements in fields like chemical sensing and nanoscale nuclear magnetic resonance.

• - Researchers used CPMG dynamical decoupling to study magnetic noise power spectra for P1 and NV centers in diamond
• - Experiments conducted on HPHT and CVD diamond samples at different magnetic field strengths
• - Interactions with 13C nuclei dominated NV power spectrum at 13 mT, reduced at 190 mT allowing background noise to exhibit a 1/ω spectrum
• - Similar behavior observed with P1 centers in CVD sample
• - Comparison made with previous measurements showing high-frequency tail from Lorentzian power spectrum
• - Resonant 13C Larmor frequency feature characterized for both P1 and NV centers using a filter function-based protocol
• - Manuscript structured into different sections: basic framework, theoretical model, key results, and insights into future experiments
• - Study provides valuable insights into understanding magnetic noise power spectra for ensembles of P1 and NV centers in diamond under different experimental conditions

SummaryResearchers used a special method to study how magnets make noise in diamonds. They did tests on different types of diamonds and at different strengths of magnet fields. They found that certain interactions with other particles affected the noise levels in the diamonds. The results were compared with past studies, showing some similarities. A specific feature related to carbon atoms was identified using a special technique. The study helps us learn more about how magnets behave in diamonds. Definitions- Researchers: People who do experiments and study things to learn new information. - Magnetic noise power spectra: How much sound or disturbance magnets make. - Diamond: A shiny, hard rock often used in jewelry. - Interactions: When things affect each other by being close together. - Experimental conditions: Different situations or settings during a scientific test or study.

Introduction: Diamond has long been recognized as a valuable material for its unique properties, including its hardness, thermal conductivity, and optical transparency. In recent years, diamond has also emerged as a promising platform for quantum technologies due to the presence of color centers such as nitrogen-vacancy (NV) and P1 defects. These defects have shown potential for applications in quantum computing, sensing, and communication. However, one major challenge in utilizing these defects is understanding and mitigating the effects of magnetic noise on their coherence. In this study, published in Physical Review B by researchers from the University of Stuttgart and Harvard University, Carr-Purcell-Meiboom-Gill (CPMG) dynamical decoupling was used to investigate the magnetic noise power spectra for ensembles of P1 and NV centers in diamond using pulsed electron paramagnetic resonance (pEPR). The experiments were conducted on both HPHT (high pressure, high temperature) diamond samples and CVD (chemical vapor deposition) diamond samples at different magnetic field strengths. Experimental Setup: The experimental setup consisted of a Bruker ELEXSYS E580 spectrometer equipped with an X-band microwave bridge operating at 2.5 GHz. A custom-built probehead was used to hold the diamond sample inside a superconducting magnet capable of generating magnetic fields up to 7 T. The pEPR measurements were performed using standard pulse sequences with varying numbers of CPMG pulses. Results: The results revealed that interactions with 13C nuclei dominated and obscured the broad features of the NV power spectrum at 13 mT. This effect was observed in both HPHT and CVD samples. However, increasing the magnetic field to 190 mT reduced the influence of these interactions on the NV centers' coherence decay rate. Furthermore, when analyzing background noise under different experimental conditions, it was found that at low frequencies (<10 kHz), there was no significant difference between the noise spectra of NV and P1 centers. However, at higher frequencies (>10 kHz), the background noise for P1 centers was found to be significantly lower than that of NV centers. The researchers also compared their results with previous measurements on single spins and small ensembles. They observed a high-frequency tail from a Lorentzian power spectrum, which is consistent with previous studies. This behavior suggests that the dominant source of magnetic noise in these systems is due to fluctuations in the local environment rather than intrinsic spin properties. Characterization of Resonant Peaks: One interesting aspect of this study was the characterization of resonant peaks in the power spectrum using a filter function-based protocol. By measuring sharp features in the power spectrum at frequencies higher than the maximum CPMG modulation frequency accessible with the system hardware, they were able to determine resonant 13C Larmor frequency features for both P1 and NV centers. Conclusion: In conclusion, this study provides valuable insights into understanding magnetic noise power spectra for ensembles of P1 and NV centers in diamond under different experimental conditions. The techniques developed in this research could have implications for various applications such as ac magnetometry and noise spectroscopy measurements in fields like chemical sensing and nanoscale nuclear magnetic resonance. Future Directions: The authors suggest several future experiments based on their findings. One potential direction is to investigate how different sample preparation methods affect coherence decay rates and background noise levels. Another avenue for further research could be exploring other dynamical decoupling sequences or optimizing existing ones to improve coherence times under different experimental conditions. Overall, this study contributes to our understanding of magnetic noise effects on quantum systems and provides useful techniques for characterizing resonant peaks in power spectra. It also highlights the importance of considering environmental factors when utilizing color center defects in diamond for quantum technologies. With further advancements, diamond-based quantum devices may become more robust against external perturbations, paving the way towards practical applications in various fields.