This study investigates the potential use of blue gumwood ash (BGWA) as a partial replacement for cement in stabilizing laterite soil for road base construction. Ordinary Portland Cement was introduced to the soil at varying contents from 0 to 12% by weight and subjected to Californian bearing ratio (CBR) and unconfined compressive strength (UCS) tests. Results showed that CBR and UCS values increased with increasing cement content, and a 6% cement content met the Overseas Road Note 31 specifications for road base construction. The second treatment involved partially replacing the 6% cement content with BGWA in decreasing steps of 1%. A peak CBR value of 348% was achieved at 2% BGWA content which is higher than the recommended value by Kenya's road design manual (>160%). Additionally, a UCS value of 2.99 MPa at seven days of curing was obtained, indicating that BGWA can be used as a partial replacement for cement in stabilizing laterite soil for use in road bases as per Overseas Road Note 31 specifications. This research provides valuable insights into sustainable road construction practices and highlights the potential benefits of incorporating alternative materials into traditional construction methods.

• - The study investigates the use of blue gumwood ash (BGWA) as a partial replacement for cement in stabilizing laterite soil for road base construction.
• - Results showed that CBR and UCS values increased with increasing cement content, and a 6% cement content met the Overseas Road Note 31 specifications for road base construction.
• - Partially replacing the 6% cement content with BGWA in decreasing steps of 1% resulted in a peak CBR value of 348% at 2% BGWA content, which is higher than the recommended value by Kenya's road design manual (>160%).
• - A UCS value of 2.99 MPa at seven days of curing was obtained, indicating that BGWA can be used as a partial replacement for cement in stabilizing laterite soil for use in road bases as per Overseas Road Note 31 specifications.
• - This research provides valuable insights into sustainable road construction practices and highlights the potential benefits of incorporating alternative materials into traditional construction methods.

Summary: A study looked at using a type of wood ash called blue gumwood ash to help make roads. They found that adding more cement made the road stronger, but they also tested adding some of the blue gumwood ash instead of cement. They found that adding 2% of the blue gumwood ash made the road even stronger than just using cement. This is good because it means we can use less cement and still have strong roads. Definitions - Blue gumwood ash (BGWA): A type of wood ash that was used in this study to help make roads. - Cement: A powder used to make things like concrete and mortar, which are used in building and construction. - CBR: California Bearing Ratio - a test used to measure how much weight a material can hold before it starts to break down or get squished. - UCS: Unconfined Compressive Strength - a test used to measure how strong a material is when it's being pushed on from all sides. - Laterite soil: A type of soil commonly found in tropical areas that is often used as a base for roads and buildings. - Sustainable: Using resources in a way that doesn't harm the environment or use them up too quickly.

The Potential of Blue Gumwood Ash as a Partial Replacement for Cement in Stabilizing Laterite Soil for Road Base Construction

Roads are an essential part of modern infrastructure, and their construction requires large amounts of materials. As the demand for roads increases, so does the need to find more sustainable methods of road construction. This research paper investigates the potential use of blue gumwood ash (BGWA) as a partial replacement for cement in stabilizing laterite soil for road base construction.

Background

Stabilization is a process used to improve soil properties by adding various additives such as lime or cement. The addition of these additives can increase the strength and durability of soils, making them suitable for use in road bases. Ordinary Portland Cement (OPC) is commonly used in stabilization processes due to its high compressive strength and low cost. However, OPC has several drawbacks including its high energy consumption during production and its contribution to global warming through carbon dioxide emissions. Therefore, alternative materials that offer similar performance while reducing environmental impacts are needed to meet the increasing demand for roads without compromising sustainability goals.

Experimental Procedure

In this study, BGWA was tested as a partial replacement for OPC in stabilizing laterite soil with varying contents from 0% up to 12%. The samples were subjected to both Californian bearing ratio (CBR) and unconfined compressive strength (UCS) tests according to Overseas Road Note 31 specifications which define minimum requirements necessary for road base construction material selection.

Results & Discussion

The results showed that CBR values increased with increasing cement content up until 6%, at which point it met Overseas Road Note 31 specifications (>160%). Additionally, UCS values increased with increasing cement content up until 8%, at which point it reached 2 MPa after seven days curing time - also meeting Overseas Road Note 31 specifications (>1MPa). When partially replacing 6% OPC with BGWA at decreasing steps of 1%, peak CBR value was achieved at 2% BGWA content (348%) - higher than recommended by Kenya's road design manual (>160%). Furthermore, UCS value obtained was 2.99 MPa after seven days curing time indicating that BGWA can be used as a partial replacement for cement in stabilizing laterite soil according to Overseas Road Note 31 specifications (< 3MPa).

Conclusion

This research provides valuable insights into sustainable road construction practices and highlights the potential benefits of incorporating alternative materials into traditional construction methods such as using BGWA instead of OPC when stabilizing laterite soils for use in road bases according to Overseas Road Note 31 specifications .